焊接工艺试验,welding procedure test
1)welding procedure test焊接工艺试验
1.This article introduces thewelding procedure test of BFe10-1-1 and 0Cr18Ni9 during the air heater manufacturing, then draws a conclusion that the excellent welding joints can be made if the welding materials are matching correctly and reasonable welding instructions and parameters are selected, and the S, P impurities are strictly controlled in the materials.简单介绍了空气加热器中BFe10-1-1与不锈钢的焊接工艺试验,并得出结论:只要 焊接工件形状匹配正确,采用合理的焊接工艺规范及参数,严格控制工件材料中的S,P等 杂质,焊角成形美观,焊接质量优良。
2.The suitable welding material and the rational welding parameters were confirmed bywelding procedure test of high strength weather resistant steel.通过对新型高强度耐候钢材进行焊接工艺试验 ,匹配合理的焊接材料 ,确定了合适的焊接工艺参数 ,并成功地应用于产品的焊接生产。
英文短句/例句
1.Study on the Disc Welding Technologic Test of Magneto Rotor永磁电机转子圆盘焊接工艺试验研究
2.Research on Welding Process of T91 Thin Steel PipeT91钢薄壁管的焊接工艺试验研究
3.Study of Vacuum Electron Beam Welding Test for Stationary Blade Carrier of Gas Turbine Compressor;燃气轮机压气机静叶环真空电子束焊接工艺试验研究
4.Welding Process Test and Application of Bottom Head and Heater Sleeve in Pressurizer稳压器下封头与加热套管的焊接工艺试验及应用
5.Qualification Test of Welding Craft for SA213-Super304H and HR3C SteelSA213-Super304H、HR3C钢焊接工艺评定试验
6.The Experimental Research on TIG Welding Process and the Joint Properties of Wrought Magnesium Alloys;变形镁合金TIG焊工艺及接头性能试验研究
7.The Experimental Research on Brazing Welding Process and the Joint Properties of YG8 Cemented Carbide;YG8硬质合金钎焊工艺及其接头性能的试验研究
8.Reasearch on the Structural Improvement of Torch and Process Experiment in Plasma-Mig Welding等离子-MIG焊接枪体结构改进及工艺试验的研究
9.Experimental Research on Vacuum Diffusion Bonding of PDC BitPDC钻头真空扩散焊接工艺正交试验研究
10.Research for VAC Synthests Reactor Weld Examination and Manufacture Scheme醋酸乙烯合成反应器焊接试验与制造工艺
11.The Welding Parameters of Ω Weld Seam Chosen on the Basis of the Methods of Orthogonal Test Design;基于正交试验设计的Ω焊缝焊接工艺参数的确定
12.Measuring the Electric Parameters of Welding Consumables and Their Usability Analysis;焊接材料焊接电参数测试及其工艺性分析
13.Study on Fusion Welding Procedure of Fe_3Al/A304 and Properties of the Jionts;Fe_3Al合金/A304不锈钢的熔焊工艺与接头性能试验研究
14.Orthogonal Optimization Test of Vacuum Diffusion Welding of Self-oscillating Pulsed Jet Nozzle of Drilling Bits石油钻头自激振荡脉冲喷嘴真空扩散焊接工艺正交试验研究
15.Controlled laser beam welding used in restoration of thin-wall ancient bronzes;可控激光束焊接薄壁青铜器工艺实验
16.Welding Torch Research and Technological Experiment for Automatic Stud Welding with Hybrid Resource复合热源自动螺柱焊焊枪装置研制及工艺试验
17.The Welding Experimentation of 12Cr1MoVG Tube Platen and Analysis of Manual Arc Welding Cracks膜式窄节距12Cr1MoVG管屏埋弧焊接试验及手工电弧焊补焊裂纹分析
18.Standard for test method of welding splice of reinforced stell bar钢筋焊接接头试验方法
相关短句/例句
operative weldability test焊接工艺性试验
3)after front the scene welding shop characteristics experiment现场焊接工艺性能试验
4)welding process performance test焊接工艺性能试验
5)welding procedure specification test焊接工艺评定试验
6)weld inspection procedure焊接检验工艺
延伸阅读
回流焊接工艺无铅技术在焊接工艺上造成的变化最大,也是整个工艺技术中最难处理的部分。这方面的变化,是来自取出铅金属后的焊接金属在熔点和表面张力上的变化。这两方面的特性变化,使原先使用在锡铅中的焊剂配方必须重新设计或调整。熔点温度的改变和焊剂成分的不同也对焊接工艺造成工艺参数上的改变。从目前的研究结果中,所有较可替代的合金中,熔点温度都高于现有的锡铅合金。例如从目前较可能被业界广泛接受的‘锡-银-铜’合金看来,其熔点是在217oC。以此作为例子来看,无铅技术的采用将在焊接工艺中造成工艺窗口的大大缩小。理论上在工艺窗口的萎缩从锡铅焊料的37oC降到只有23oC,约38%的萎缩(见图一)。实际上,工艺窗口的萎缩还比以上的理论值还大。原因是在实际工作上,我们的测温(Profiling)做法含有一定的不确定性,加上DFM的限制,以及要很好的照顾到焊点‘外观’(不少工厂还是以外观做为主要的质量检查依据)等等,这个回流焊接工艺的窗口其实只约有14oC(约53%的萎缩)。这只有14oC的工艺窗口,事实上在工艺调制上是有很大的挑战性的。而对设备(回流炉)和DFM的要求也比锡铅技术的应用要求高出许多。 理论上在焊接过程时,焊点的温度只要达到焊料合金的熔点温度就行了。但在实际情况下,刚达到熔点温度的焊料,其润湿性特差。所以我们必须提高实际焊点的温度以增加润湿能力。由于无铅合金的润湿性比起锡铅合金还差,这做法在无铅技术上更是必要。PCBA上的器件和板材都有承受温度的极限,目前在无铅技术中对这承受温度提出的要求是260oC。虽然这温度和含铅技术的240oC比较下有所提高,但因为焊点温度受到熔点温度和润湿性考虑的影响提高的幅度更大,这就造成了容许的工艺窗口(温度的上下限)在无铅技术中小了许多。 事实上,如果器件供应商在器件设计上只满足国际建议的260oC为上限,用户所面对的问题还更大。所拥有的焊接温度工艺窗口就可能连上面所说的14oC都不到了。这是因为有些器件如BGA之类的封装设计,在对流加热的应用中,封装本体的温度是常常高于底部的焊点温度的。这原本还不算是个大问题,使问题恶化的是,这些器件一般也都是热容量较大的器件,封装导热性不是十分优良。而由于同一PCBA上总有些热容量小很多的器件(注三),所以就造成了实际温差十分难通过工艺调整来缩小和确保都在工艺窗口内。 不只是工艺窗口的缩小给工艺人员带来巨大的挑战,焊接温度的提高也使焊接工作更加困难。其中一项就是高温焊接过程中的氧化现象。我们都知道,氧化层会使焊接困难、润湿不良以及造成影响焊点寿命的虚焊。而氧化的程度,除了器件来料本身要有足够的控制外,用户的库存条件和时间、加工前的处理(例如除湿烘烤)、以及焊接中预热(或恒温)阶段所承受的热能(温度和时间)等等都是决定因素。无铅技术的温度提高,正使焊端在预热段造成更多的氧化。如果锡膏的助焊剂能力不足,或是回流温度曲线在‘清洁/除氧化’段的工艺设置不当的话,回流时就可能出现焊接不良的问题。