垫层混凝土裂缝调查,investigation of cushion concrete crack
1)investigation of cushion concrete crack垫层混凝土裂缝调查
英文短句/例句
1.The Investigation and Processing Scheme of Cushion Concrete Crack of Zaoshi Dam皂市大坝垫层混凝土裂缝调查和处理方案
2.Investigation Analysis And Treatment Of Concrete Crack“七天酒店”混凝土裂缝的调查分析与处理
3.Survey and countermeasures of crack on hollow brick wall made of granite residue concrete石渣粉混凝土空心砌块墙体裂缝调查与对策分析
4.autogenous healing of concrete混凝土裂缝自行愈合
5.Cause of Cracks of Tianjin Port High-pile Wharf Surface Layer Concretes and Its Control Measures天津港高桩码头面层混凝土裂缝成因分析及裂缝控制技术措施
6.Analysis and Treatment of Underground Concrete Wall Cracks of High-rise Buildings高层地下混凝土墙体裂缝的分析与处理
7.Study on Equivalent Strength of Crack Director and Fracture of Layer Surfaces in RCC Dam;碾压混凝土坝诱导缝等效强度及层面断裂研究
8.Research on Crack Control of High-rise Building Super-length Mass Concrete Foundation Slabs;高层建筑超长大体积混凝土底板裂缝控制研究
9.Study on the Initiation and Propagation Mechanism of Reflection Crack in Asphalt Concrete Overlays;沥青混凝土加铺层反射裂缝的形成与扩展研究
10.Concrete Slab Cracks of High-Rises;高层现浇钢筋混凝土楼板裂缝问题剖析
11.EXPERIMENTAL RESEARCH ON THE EFFECTS OF SURFACE REINFORCEMENT ON CRACK SPACING AND WIDTH OF REINFORCED CONCRETE BEAMS表层钢筋对混凝土梁的裂缝影响试验研究
12.The experimental study on the concrete protective layer rust expansion crack expansion混凝土保护层锈胀裂缝扩展的试验研究
13.Crack control measures for concrete exterior wall of high-rise building basement浅析高层地下室混凝土外墙裂缝控制技术措施
14.Analysis of crack control of raft foundation concrete in a high building某高层建筑筏板基础混凝土裂缝控制分析
15.Control of cracks in concrete small hollow block wall of multistoried house多层住宅混凝土小型空心砌块墙体裂缝控制
16.Construction technology of concrete temperature crack prevention in high-rise building高层建筑房屋防止混凝土温度裂缝的施工技术
17.Analysis of Causation for Cracks in Surface Concrete-layer of New Docks Built in Summer夏季新建码头混凝土面层裂缝的原因分析
18.Study-Ⅱ of corrosive crack width on reinforcement concrete cover钢筋混凝土保护层锈胀裂缝宽度研究Ⅱ
相关短句/例句
cushion concrete crack treatment垫层混凝土裂缝处理
1.To meet the construction needs ofcushion concrete crack treatment of Zaoshi Hydraulic Project Dam Engineering, in line with design requirement,the contractor tests for the on-site chemical grouting in order to definite construction parameters, work out chemical grouting treatment scheme for cushion concrete crack and guide the construction.为满足皂市水利枢纽大坝工程垫层混凝土裂缝处理施工需要,承包人按设计要求进行现场化学灌浆试验,通过试验确定施工参数,制订垫层混凝土裂缝化学灌浆处理的施工技术方案,指导垫层混凝土裂缝化学灌浆处理的施工。
3)concrete crack混凝土裂缝
1.Analysis ofconcrete cracks of one archives building;某框架结构档案馆工程混凝土裂缝分析
2.Causes of theconcrete crack in hydraulic pier and its crack resistant measures;水工墩墙混凝土裂缝成因和防裂措施
3.The structure design andconcrete crack controlling;结构设计及混凝土裂缝的控制
4)concrete cracks混凝土裂缝
1.Causes of liningconcrete cracks of tunnel and its prevention: taking Erdaowan Tunnel as an example;浅谈隧洞衬砌混凝土裂缝产生的原因及预防措施——以二道弯隧洞为例
2.Causes and control ofconcrete cracks;混凝土裂缝的原因分析和控制措施
3.Analysis and prevention measures of theconcrete cracks in hydraulic tunnel project;水工隧洞衬砌混凝土裂缝成因分析及控制措施
5)Crack of concrete混凝土裂缝
6)concrete cracking混凝土裂缝
1.The prevention of linerconcrete cracking at tailwater tunnels and measures on different levels cracking are discussed in detail.水工隧道混凝土衬砌均存在不同程度的裂缝,本文介绍了尾水隧洞衬砌混凝土裂缝预防和不同类型裂缝的处理办法。
2.The results show that theconcrete cracking can be prevented by using suitable internal water-pipe cooling and external heat preservation.水化放热过程中,混凝土产生内外温差和上下层温差,而温差、自生体积收缩变形、干缩和约束等是混凝土裂缝形成的主要原因。
延伸阅读
大型设备基础混凝土裂缝防治大型设备基础混凝土裂缝防治protection and treatment for crack during construction of large volume foundationdaxlng shebe一Jiehu hunningtu}iefeng fangZhl大型设备蓦础混凝土裂缝防治(proteetion。ndtreatment for eraek during eonstruetion of large vol-ume foundation)在冶金工厂建设中，设备基础的混凝土约占混凝土工程总量的60%以上。随着冶金设备向大型化发展，设备基础的体积愈趋庞大。以中国上海宝钢工程为例，容积为4063m“的1号高炉，其基础混凝土工程量约为600om3;3座3oot转炉的基础底板的混凝土工程量将近700om“。施工时每次混凝土的浇筑量多在looom3以上。施工中，水泥水化热引起混凝土浇筑块体内部温度和温度应力剧烈变化，以及混凝土的凝结收缩，都会引起对结构整体性、耐久性和强度有影响的混凝土裂缝。防止这种裂缝的产生和对已出现裂缝的有效治理是保证工程质量的关键之一。裂缝原因和防止原则在大型设备基础的施工中，当混凝土内部温度变化和凝结收缩引起的变形受到约束时，浇筑块体内就要产生应力。当其中的拉应力超过混凝土材料的抗拉极限时就会出现裂缝。对变形的约束有两类情况:一是混凝土浇筑块体内部各质点间因变形量不同而产生相互牵制和影响，称为“自约束”;二是浇筑块体的变形受到外部物体(如地基、相邻结构、下部混凝土浇筑层等)的阻碍，称为“外约束”。为防止裂缝的产生，应从以下几个方面考虑对策。(1)提高混凝土自身和混凝土结构的抗裂能力。施工中要严格控制材料和施工工艺，使结构质量完全符合设计和规范要求。(2)减少混凝土中的总发热量，降低水泥水化发热速率，合理调剂混凝土在凝结过程中的温度与湿度，以减小温度应力和收缩产生的应力。(3)减弱内、外约束的影响。(4)重视控制温度对防止裂缝产生的决定性作用，在基础施工的全过程中，按阶段进行温度应力分析，确定温度控制指标和技术措施。沮控防裂措施包括基础设计、混凝土配制、混凝土浇筑与养护、施工中混凝土温度监测四个方面。基础设计主要措施有:(1)基础混凝土的强度等级应为C巧一C25。(2)对独立的大型钢筋混凝土设备基础不设沉降缝、温度缝等永久变形缝。(3)当基础设置于岩石地基上时，在混凝土垫层上表面应设滑动层(可采用一毡二油构造)，以减少地基对混凝土变形的约束。(4)基础配筋除应满足基础承载力及构造要求外，还要增配承受因水泥水化热引起的温度应力及控制裂缝开展的构造钢筋。混凝土配制主要措施有:(1)选定混凝土配合比时，应在保证基础强度、耐久性和施工工艺要求的前提下尽量减少水泥用量，以降低混凝土的绝对温升值。